The maximum dispersion amount of α - Fe_2O_3 on NaY zeolite measured with XRD quantitative phase analysis is 0.060 g α - Fe_2O_3 / gNaY , which is only 5.5 % of the monolayer capacity of α - Fe_2O_3 on NaY according to a close-packed monolayer model .

经XRD相定量外推法测定，α-Fe2O3在NaY沸石上的最大分散量为0.060gα-Fe2O3/gNaY，仅占α-Fe2O3在沸石表面密置单层量的5.5%。

Proper addition of MgO and La_2O_3 increased the monolayer dispersion capacity of NiO on Al_2O_3 , and caused the crystal size of nickel to become smaller .

适量的MgO和La2O3能增加NiO在Al2O3上的单层分散容量，并使还原得到的Ni晶粒变小。

The spin conversion of Ps becomes weaker with NiO content exceeding monolayer dispersion capacity , the prohibition effect of Ps formation by crystalline NiO is significant .

当NiO含量超过单层分散量时，Ps的自旋转换逐渐减弱，晶态NiO对Ps形成有明显的禁止效应。